Compund Symbol |
λmax nm |
Λm Ω−1mol−1cm2 |
μeff. (B.M.) |
Transitions | Geometry |
---|---|---|---|---|---|
S.TH Ligand |
638, 538, 468, 427 358, 338. 266, 222, 210. |
||||
S.TH-Ag 1:1 |
633, 534, 443, 349, 260, 224. |
33.27 | Diamagnetic | no d-d transition | Square planar |
S.TH-Co 2:1 |
632, 538, 467, 429, 379, 354, 293. 261, 229. |
120.21 | 5.24 | s 4T1g → 4T2g(F)(ν1), 4T1g → 4A2g(F)(ν2) 4T1g → 4T1g(P)(ν3) | Octahedral |
S.TH-Cr 2-1 |
637, 538, 455, 375, 350, 275. 260, 227, 215. |
114.16 | 3.71 | 4B1g → 4Eg (4T2g), II: 4B1g → 4B2g(4T2g), III: 4B1g → 4E g(4T1g), IV: 4B1g → 4A2g(4T1g) V: 4B1g → 4A2g(4T1g (P)), VI: 4B1g → 4E2g (4T1g (P) | Octahedral |
S.TH- Cu 2-1 |
633, 588, 536, 469, 410,375, 335, 274. 250, 227. |
14.96 | 2.11 | 2B1g→2B2g, 2B1g→2Eg, 2B1g →2A1g |
Octahedral |
S.TH-Ni 2:1 |
638, 537, 467,403, 366, 323, 278. 250, 227. |
11.67 | 3.04 | 3A2g → 3T1g(P)(ν1), 3A1g → 3T2g(F)(ν2) and 3A2g→ 1Eg | Octahedral |
S.TH-Zn 2:1 |
636, 538, 461, 401. 362,253, 221. |
16.07 | Diamagnetic | no d-d transition | Octahedral |