Table 2: Experimental results of mechanical properties of composite slurry.
Experimental group |
Bending strength (MPa) |
Unconfined compressive strength (MPa) |
3d |
7d |
14d |
28d |
3d |
7d |
14d |
28d |
1 |
1.99 |
2.34 |
4.15 |
5.39 |
9.51 |
12.34 |
16.75 |
21.38 |
2 |
0.48 |
0.75 |
0.81 |
1.11 |
1.50 |
2.82 |
3.31 |
4.32 |
3 |
0.65 |
1.11 |
1.60 |
2.21 |
2.48 |
3.85 |
5.03 |
8.18 |
4 |
0.29 |
0.30 |
0.70 |
1.13 |
0.96 |
1.43 |
2.61 |
3.57 |
5 |
1.64 |
2.08 |
3.88 |
5.01 |
7.36 |
10.02 |
12.66 |
19.81 |
6 |
0.31 |
0.66 |
1.81 |
2.51 |
2.24 |
2.36 |
3.14 |
4.52 |
7 |
0.97 |
1.49 |
2.00 |
2.63 |
4.28 |
4.74 |
7.36 |
9.28 |
8 |
0.32 |
0.60 |
0.81 |
1.22 |
1.74 |
2.31 |
3.16 |
4.19 |
9 |
2.01 |
2.25 |
3.99 |
5.18 |
8.38 |
11.78 |
16.03 |
21.44 |
10 |
0.56 |
0.82 |
1.01 |
2.20 |
2.25 |
4.37 |
6.02 |
8.32 |
11 |
0.31 |
0.51 |
0.79 |
1.47 |
1.11 |
2.52 |
3.23 |
4.29 |
12 |
0.38 |
0.52 |
0.76 |
1.31 |
1.64 |
2.92 |
3.27 |
4.31 |
13 |
1.38 |
2.13 |
3.74 |
4.95 |
7.34 |
11.37 |
14.68 |
20.17 |
14 |
0.54 |
0.74 |
1.19 |
2.35 |
2.25 |
3.76 |
4.28 |
8.01 |
15 |
0.94 |
0.98 |
1.63 |
2.30 |
3.82 |
4.24 |
5.78 |
9.35 |
16 |
0.31 |
0.32 |
0.65 |
1.24 |
1.30 |
1.82 |
2.21 |
3.72 |