Specimens | Tested Ultimate Strength Pt(kN) | Statistic Analysis of Pt | |
---|---|---|---|
Mean value of Pt (kN) |
Holes influence | ||
AC-11-SH-1 | 56.55 | 54.84 | 9.58% |
AC-11-SH-2 | 54.90 | ||
AC-11SH-3 | 55.15 | ||
AC-11-SH-4 | 53.10 | ||
AC-11-SH-5 | 57.45 | ||
AC-11-SH-6 | 51.90 | ||
AC-21-SH-1 | 56.85 | 54.70 | 9.82% |
AC-21-SH-2 | 55.40 | ||
AC-21-SH-3 | 56.85 | ||
AC-21-SH-4 | 52.75 | ||
AC-21-SH-5 | 52.50 | ||
AC-21-SH-6 | 53.85 | ||
AC-12-SH-1 | 51.45 | 52.15 | 14.02% |
AC-12-SH-2 | 53.10 | ||
AC-12-SH-3 | 54.60 | ||
AC-12-SH-4 | 50.25 | ||
AC-12-SH-5 | 51.30 | ||
AC-12-SH-6 | 52.20 | ||
AC-22-SH-1 | 50.30 | 50.46 | 16.81% |
AC-22-SH-2 | 48.95 | ||
AC-22-SH-3 | 51.20 | ||
AC-22-SH-4 | 52.05 | ||
AC-22-SH-5 | 49.85 | ||
AC-22-SH-6 | 50.40 | ||
AC-00-NH-1 | 61.03 | 60.66 | / |
AC-00-NH-2 | 60.28 |