Long Term Water Storage Deteriorates Bonding of Composite Resin to Alumina and Zirconia Short Communication

T.T. Heikkinen1, J.P Matinlinna2, P.K. Vallittu1, *, L.V.J. Lassila1
1 Department of Biomaterials Science and Turku Clinical Biomaterials Centre – TCBC, Institute of Dentistry, University of Turku, Turku, Finland
2 University of Hong Kong, Faculty of Dentistry, 4/F Dental Materials Science, The Prince Philip Dental Hospital, Hong Kong


Objective of this study was to evaluate the effects of long term water storage and ageing on the bond strength of resin composite cement to yttria-stabilized zirconium dioxide (zirconia) and dialuminium trioxide (alumina). Substrate specimens of alumina and zirconia were air particle abraded with dialuminium trioxide before priming and application of composite resin. Priming was made with gamma metharyloxy-trimethoxysilane or acryloxypropyl-trimethoxysilane monomer after which the intermediate dimethacrylate resin was applied and photopolymerized. This was followed by curing particulate composite resin cement (Relyx ARC) to the substrate as a resin stub. The ageing methods of the specimens (n=6) were: (1) they stored four years in 37±1ºC distilled water, (2) thermocycled 8000 times between 55±1ºC and 5±1ºC, (3) stored first in water for four years and then thermocycled. Specimens which were stored dry, were used as controls. Bonding of composite resin was measured by shear-bond strength test set-up. Both thermocycling and long-term water storage decreased significantly shear bond strength values compared to the control group (from the level of 20 MPa to 5 MPa) regardless of the used primer or the type of the substrate. Combination of four years water storage and thermocyling reduced the bond strength even more, to the level of two to three megapascals. In can be concluded that water storage and thermocycling itselves, and especially combination of water storage and thermocycling can cause considerable reduction in the bond strength of composite resin cement to alumina and zirconia.

Keywords: : Zirconia, alumina, bond strength, composite.

Article Information

Identifiers and Pagination:

Year: 2013
Volume: 7
First Page: 123
Last Page: 125
Publisher Id: TODENTJ-7-123
DOI: 10.2174/1874210601307010123

Article History:

Received Date: 3/6/2013
Revision Received Date: 16/8/2013
Acceptance Date: 3/9/2013
Electronic publication date: 30 /9/2013
Collection year: 2013

© Heikkine et al.; Licensee Bentham Open.

open-access license: This is an open access article licensed under the terms of the Creative Commons Attribution Non-Commercial License ( which permits unrestricted, non-commercial use, distribution and reproduction in any medium, provided the work is properly cited.

* Address correspondence to this author at the Institute of Dentistry, University of Turku, Lemminkäisenkatu 2, FI-20520 Turku, Finland, Tel: +358-2-3338332; Fax: +358-2-3338330; Email:


"Thank you for your magnificent and marvelous support throughout the publication stages. I would like to endorse my experience with you as a Junior Researcher and a recent graduate of the Dental school. Once again Thank you for your Great Help and Guidance throughout the stages of Publication. You guys are a great team and I am proud to be a Young Bentham author."

Asra Sabir Hussain
The University of Edinburgh Business School, UK

"My experience with Bentham Open was a valuable one because the quality of the services and analysis of my paper contributed in improving what we intended to convey to the readers."

José Ricardo Kina
Department of Surgery and Integrated Clinic,
Araçatuba School of Dentistry, São Paulo State University

"The Publication Manager was very cooperative and replied my mails and guided me without any delays; however the reviewing process was too long."

Mahtab Memarpour
Prevention of Oral and Dental Disease Research Center,
Department of Pediatric Dentistry, School of Dentistry,
Shiraz University of Medical Sciences, Shiraz,

Browse Contents

Webmaster Contact:
Copyright © 2020 Bentham Open